Sino Composite offers FRP I Beams with high strength, light weight, and excellent corrosion resistance. We provide various types of FRP I beams, which are an integral part of our FRP building system. At the same time, we can provide customized beams processing.
모델 | 치수(mm) | 대략적인 무게 |
1-HB76 | 76x76x6.4 | 2.67 |
2-HB102 | 102x102x6.4 | 3.59 |
3-HB102 | 102x102x8.0 | 4.50 |
4-HB152 | 152x152x6.4 | 5.43 |
5-HB152 | 152x152x9.5 | 8.10 |
6-HB203 | 203x203x9.5 | 10.80 |
7-HB203 | 203x203x12.7 | 14.36 |
8-HB254 | 254x254x9.5 | 13.60 |
9-HB254 | 254x254x12.7 | 18.04 |
10-HB305 | 305x305x12.7 | 21.50 |
1-IB50 | 50x102x6.4 | 2.40 |
2-IB76 | 76x152x6.4 | 3.59 |
3-IB76 | 76x152x9.5 | 5.32 |
4-IB102 | 102x152x9.5 | 6.00 |
5-IB102 | 102x203x9.5 | 7.20 |
6-IB102 | 102x203x12.7 | 9.50 |
7-IB127 | 127x254x9.5 | 9.00 |
8-IB127 | 127x254x12.7 | 11.90 |
| 기계적 특성 | ASTM | 단위 | VALUE |
| 인장 강도 LW | D-638 | Mpa | 207 |
| 인장 강도 CW | D-638 | Mpa | 48 |
| 인장 계수 LW | D-638 | Gpa | 17.2 |
| 인장 계수 CW | D-638 | Gpa | 5.5 |
| 압축 강도 LW | D-695 | Mpa | 207 |
| 압축 강도 CW | D-695 | Mpa | 103 |
| 압축 계수 LW | D-695 | Gpa | 17.2 |
| 압축률 CW | D-695 | Gpa | 6.9 |
| 굴곡 강도 LW | D-790 | Mpa | 207 |
| 굴곡 강도 CW | D-790 | Mpa | 69 |
| 굴곡률 LW | D-790 | Gpa | 12.4 |
| 굴곡률 CW | D-790 | Gpa | 5.5 |
| 탄성 계수 E | 전체 섹션 | Gpa | 19.3 |
| 전단 계수 | / | Gpa | 3.1 |
| 짧은 빔 전단 | D-2344 | Mpa | 31 |
| 펀치 전단 | D-256 | Mpa | 69 |
| 베어링 강도 LW | D-953 | Mpa | 207 |
| 노치형 이조드 임팩트 LW | D-256 | KJ/m | 1.33 |
| 노치형 이조드 임팩트 LW | D-256 | KJ/m | 0.21 |
| 물리적 속성 | ASTM | 단위 | VALUE |
| 바콜 경도 | D-495 | / | 45 |
| 24시간 수분 흡수 | D-570 | 최대 % | 0.45 |
| 밀도 | D-792 | g/cm³ | 1.72-1.94 |
| 열팽창 계수 | D-696 | 10-6in/in/℃ | 8 |
| 전기적 특성 | ASTM | 단위 | VALUE |
| 아크 저항 LW | D-485 | 초 | 120 |
| 유전체 강도 LW | D-149 | Kv/in | 35 |
| 유전체 강도 CW | D-149 | 볼트/밀 | 200 |
| 유전체 강도 PF | D-150 | @60hz | 5 |
| 가연성 속성 | ASTM | 단위 | VALUE |
| 터널 테스트 | E-84 | 화염 속도 | 최대 25개 |
| 인화성 | D-635 | / | 비연소 |